Polypropylene Concrete Strengthening Fibers High Tenacity Monofilament Type

Polypropylene Concrete Strengthening Fibers High Tenacity Monofilament Type

Polypropylene Fiber (PP Fiber)

Denier count: 1.2D-18D

Cut length: 4mm-128mm

Features:

- It is produced by direct spinning with polymer as the raw material.

- High tenacity, few defect, good crimping performance, moderate OPU, low hot air shrinkage, good spin ability, soft and smooth hand feeling, high standards of fiber resultant yarn quality, low yarn irregularity and wide applications

- With high modulus and tenacity, low elongation, bright color and good spinnability

- Main usage: for spinning, non-woven, spunlace, sewing thread, carpet thread, etc.

We have been exporting these fibre for more than ten years, we are able to offer you the suitable fibre for your construction, we have more than 6 type fibre which be mixed with concrete for road making, construction, pls contact us for details if you have any interesting, thank you in advance.

Fiber Item:

1. PP Fiber Monofilament Form

Raw Material : Polypropylene

Crack Elongation : 20%±5%

Type : Monofilament

Density : 0.91±0.01 % g/cm3

Fiber Diameter : 0.02-0.05±0.005mm

Melting Point : 160---170?/p>

Tensile Strength : ≥450MPa

Resistance to Acid,Alkali : Strong

Size : 4mm,6mm,10mm,12mm,15mm,18mm,20mm,24mm,40mm

Water Absorbency : No

2. PP Fiber Mesh Form

Density(g/cm3) : 0.91

Elastic Modulas (MPa) : >3500

Length(mm) : 6mm,10mm,12mm,15mm,20mm,50mm

Equivalent Diameter (m) : 100

Shape : Beam-like Net

Crack Elongation(%) : ≥10

Acid &Alkali Resistance : Strong

Water-Absorbency : No

Tensile Strength(MPa) : 346-560

Melting Point(C) : 160—170

3. PP Fiber Bunchy Twisted Form

Density(g/cm3) : 0.91

Elastic Modulus ( MPa) : >5000

Length(mm) : 54mm

Equivalent Dia (mm) : 0.3+/- 0.05

Shape : bundle-like and twisted

Break tensile Ratio(%) : >15

Break Strength(MPa) : >560

Resistance to acid, alkali : strong

4. Curved PP Macro Fiber

Density(g/cm3) : 0.91

Elastic Modulas (MPa) : >5000

Length(mm) : 30mm,40mm,50mm

Equivalent Dia(μm) : 80,100

Shape : curved bar

Break Tensile Ratio(%) : ≤155

Break Strength(MPa) : ≥460

Melt Point : ≥160

Packing:

20kgs plastic woven bag / 1kg water-soluble bag /1000kgs jumbo bag

Company Overview

Anhui Herrman Impex Co., Ltd. is a privately owned enterpirse with more than Twenty-two years' experiences of foreign trade. Its former shape came from Anhui Herrman Chemicals Co., Ltd., which established in 1994 and devoted itself into the exportation and importation business of Chemicals and Light Industry.

In order to shape an uniform and scientific management system with high efficiency, normalize the operation process and guarantee the advancement of the company in a long term, we made Herrman Chemicals and Herrman Light Industries become one: Anhui Herrman Impex Co., Ltd., which is acknowledged as the headquarters of Herrman group. At the same time, it points out the way we are moving. In 2002, we were certified and approved by ISO9001:2000 Quality System, details of which have been carried out since then and provided strong foundation for normalized management and standard service of the company.

To meet the requirement of company progress, we started Shanghai Herrman Impex Co., Ltd., Nanjing Herrman Chemical Factory, Nelson International Inc. and Anhui Herrman Titanium Dioxide Co., Ltd. in the same year of 2002. All these efforts have been proved to be with important significance in the process of being an industry company.

In a response to rapidy growing machinery business, we set up another specialized company Anhui Herrman Machinery & Technology Co., Ltd. In 2010, responsible for all machinery business.

Looking back and forward, we will keep advancing for the brighter future without hesitation.

Certifications